The Effect of Oxygen, Nitrogen, and Hydrogen on the Mechanical Properties of Cb-752

[+] Author and Article Information
M. W. Mahoney, N. E. Paton

North American Rockwell Science Center, Thousand Oaks, Calif.

J. Eng. Mater. Technol 96(3), 201-206 (Jul 01, 1974) (6 pages) doi:10.1115/1.3443211 History: Received October 15, 1973; Revised February 22, 1974; Online August 17, 2010

Abstract

Uniaxial tensile properties of the niobium-base alloy Cb-752 have been determined as a function of oxygen, nitrogen, and hydrogen content over a temperature range of −196 C to 200 deg C. Each of these impurities increased the temperature at which a ductile-brittle transition occurs. Although ductility was severely reduced, strength parameters were relatively unchanged making detection of embrittlement by hardness testing difficult. Impurity levels for embrittlement were sufficiently low and the affinity of Cb-752 for contamination sufficiently great that processing operations require strict control. The mechanism of this impurity embrittlement is not well understood. However, observations of fracture surfaces of brittle failures reveal mixed intergranular cleavage with a uniform distribution of precipitates throughout grain boundaries. These observations are discussed in the light of current theories.

Copyright © 1974 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In