Fatigue Crack Growth Resistance of Several Neutron Irradiated Pressure Vessel Steels and Welds

[+] Author and Article Information
P. Shahinian, H. E. Watson, J. R. Hawthorne

Metallurgy Division, Naval Research Laboratory, Washington, D. C.

J. Eng. Mater. Technol 96(4), 242-248 (Oct 01, 1974) (7 pages) doi:10.1115/1.3443237 History: Received January 25, 1974; Revised March 05, 1974; Online August 17, 2010

Abstract

Pre and postirradiation fatigue crack growth rates in A302-B, A533-B, and A543 steel plate and in two A543 welds (submerged arc and electroslag) were determined at 550 deg F (288 deg C) in air. The fracture mechanics approach was used to analyze the experimental data. Neutron irradiation at 585 deg F (307 deg C) to 2.5 × 1019 n/cm2 , > 1 MeV produced no significant effect on resistance to crack growth in A302-B steel and caused only a slight decrease in crack growth resistance of A533-B and A543 steels. Also, the resistance to crack growth of the submerged arc weld was unaffected by the irradiation, but that of the electroslag weld was substantially improved. The crack growth rate versus stress intensity factor range curve for the A302-B steel represents an upper bound for the pre and postirradiation data for the steels and welds of this study.

Copyright © 1974 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In