A Case History of Cracking Failures in Deformed Austenitic Alloy Pipe Operating in the Temperature Range of 1000-1300 Deg F (538-705 Deg C)

[+] Author and Article Information
G. B. Kohut

Gulf Research and Development Co., Materials and Equipment Division, Houston, Tex.

J. Eng. Mater. Technol 97(4), 316-321 (Oct 01, 1975) (6 pages) doi:10.1115/1.3443305 History: Received March 11, 1975; Online August 17, 2010

Abstract

The results of several cracking failures in fabricated austenitic alloy pipe are reported in detail. These failures were a result of cracking which occurred at the operating temperature in zones which exhibited deformation. The failure analysis included metallography, mechanical and stress rupture tests, electron microscopy and electron microprobe scanning. Although a firm conclusion on the cause of cracking could not be reached, it was obvious that the deformation induced in the pipe during fabrication played a significant role in the failure and in the loss of rupture tensile ductility.

Copyright © 1975 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In