Fast Burst Reactor Burst Rod Adaptor Failure Analysis

[+] Author and Article Information
W. C. Hull

Mechanical Engineering Department, New Mexico State University, Las Cruces, N. Mex.

A. De La Paz, D. L. Welch

Nuclear Weapons Effects Branch, Applied Sciences Division, Army Missile Test and Evaluation Directorate, White Sands Missile Range, N. Mex.

J. Eng. Mater. Technol 99(1), 86-92 (Jan 01, 1977) (7 pages) doi:10.1115/1.3443413 History: Received March 15, 1976; Revised June 18, 1976; Online August 17, 2010

Abstract

Failure of a 440C stainless steel burst rod adaptor from the White Sands Missile Range Fast Burst Reactor is analyzed. The operational history of the adaptor, including nature of loading, radiation accumulation, and thermal environment, was examined. Problems associated with handling radioactive materials were overcome through careful monitoring and disposal. The chemical composition of the adaptor material was checked by x-ray and electron probe spectroscopy. The failure surface was examined and photographed at various magnifications, using optical and scanning electron microscopes. Areas of crack origin, rapid fracture, final breakoff, and abrasion from rebound are identified. Metallographic specimens were prepared, the grain structure examined, and hardness profiles obtained. The grain structure indicated the presence of microvoids and carbide segregation, and slight hardening was noted. Failure occurred at the base of a male thread in a region showing significant tool markings. Examination of the failure surface indicated crack initiation due to Stage I fatigue followed by rupture from shock overload. Recommendations to avoid similar occurrences are given.

Copyright © 1977 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In