Growth Characteristics of a Fatigue Crack Approaching and Growing Beneath an Adhesively Bonded Doubler

[+] Author and Article Information
J. M. Anderson

Georgia Institute of Technology, Atlanta, Ga.

C. S. Chu, W. M. McGee

Lockheed-Georgia Company, Marietta, Ga.

J. Eng. Mater. Technol 100(1), 52-56 (Jan 01, 1978) (5 pages) doi:10.1115/1.3443450 History: Received August 18, 1977; Online August 17, 2010

Abstract

The title problem was investigated experimentally and numerically. Aluminum adherends and two adhesives, AF-55 and AF-127, were utilized in the investigation. Each specimen had a crack introduced at an undoubled edge. Fatigue cycles with a fixed average remote-stress maximum of 103.4 MPa at a stress ratio of 0.1 were applied to grow the initial crack up to and beneath the doubler. Crack-growth rates were measured to assess the inhibiting effect of the doubler, and ultrasonic scans were made to determine debond-zone shapes. After each crack had grown approximately halfway beneath the doubler, a secondary crack initiated at the edge of the doubler, precipitating rupture of the specimen. A finite-element model of the specimen employed a singularity element to represent the crack-tip neighborhood and shear springs to represent the adhesive layer. Springs were released in the model to simulate local debonding. The stress-intensity factor was computed as a function of crack length for linear and nonlinear representations of the two adhesives used in the experimental program.

Copyright © 1978 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In