Producing a Tough, High Strength Cast Steel Free of Temper Embrittlement

[+] Author and Article Information
S. Floreen

The International Nickel Co., Inc., INCO Research & Development Center, Sterling Forest, Suffern, N. Y. 10901

J. Eng. Mater. Technol 101(1), 98-103 (Jan 01, 1979) (6 pages) doi:10.1115/1.3443659 History: Received June 27, 1978; Revised September 02, 1978; Online August 17, 2010

Abstract

Temper embrittlement of a cast 3Ni-3Cr steel was produced by small amounts of either P or Mn in samples tempered at 650°C and air cooled. Auger spectroscopy examinations showed P embrittlement was produced by cosegregation of P, Ni, and Cr. Embrittlement by Mn appeared to be caused by Mn and S segregation. In coarse grained materials fractures were intergranular. In fine grained material, both intergranular and brittle transgranular fractures were observed, and Auger mapping showed impurity enrichment on transgranular fracture surfaces. Segregation and fracture on martensite packet boundaries is suggested as the origin of the transgranular fracture. Changing the tempering temperature and adding a half percent Mo solved the embrittlement problem. Water quenching was not required. A 150 mm thick casting of the new composition showed good tolerance for P and Mn, a yield strength of 500 MPa, and good toughness down to −80°C.

Copyright © 1979 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In