Fatigue Crack Propagation Beyond General Yield

[+] Author and Article Information
Öktem Vardar

Department of Mechanical Engineering, Boğaziçi University, Istanbul, Turkey

J. Eng. Mater. Technol 104(3), 192-199 (Jul 01, 1982) (8 pages) doi:10.1115/1.3225064 History: Received June 15, 1981; Online September 15, 2009

Abstract

Tests are carried out on compact tension specimens of AISI 1020 hot-rolled steel at nominal stress levels beyond yield. The results show that crack propagation rates can be correlated successfully using an operational definition of the range ΔJ of the J-integral. The rate of crack growth per cycle da/dN is shown to be related to ΔJ by da/dN=A (ΔJ)α for conditions ranging from linear elastic to limit load. The exponent α agrees well with other published data on low strength steels and the quantity A is found to have a weak dependence on frequency. Examination of the fracture surface reveals that static failure modes are operating at the high crack propagation rates.

Copyright © 1982 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In