Hydrogen-Induced Crack Propagation in a QT-Steel Weldment

[+] Author and Article Information
B. A. B. Andersson

Division of Solid Mechanics, Chalmers University of Technology, Gothenburg, Sweden

J. Eng. Mater. Technol 104(4), 249-256 (Oct 01, 1982) (8 pages) doi:10.1115/1.3225072 History: Received April 01, 1982; Online September 15, 2009

Abstract

A hydrogen-induced fracture process in the HAZ of a QT-steel weldment is studied numerically. Two-dimensional models are used to estimate the transient distributions of stress and hydrogen during the cooling and during the subsequent crack propagation. The distributions of hydrogen in front of a blunted crack are studied for different void volumes in the fracture zone corresponding to brittle and ductile fracture mechanisms. It is tentatively concluded that the incubation time at slow crack growth is not controlled by the hydrostatic stress. A ductile fracture mechanism leading to a relative void volume of 0.02-0.05 in the fracture zone is found to imply long incubation times resulting in a low average crack propagation speed.

Copyright © 1982 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In