High Carbon Steel Microcracking Control During Hardening

[+] Author and Article Information
J. Lyman

University of Maine at Orono, Orono, Maine

J. Eng. Mater. Technol 106(3), 253-256 (Jul 01, 1984) (4 pages) doi:10.1115/1.3225711 History: Received July 11, 1983; Online September 23, 2009


When high carbon, low alloy steels, such as AISI 52100, are conventionally quenched or marquenched from an austenitizing temperature that dissolves all of the carbon in the austenite, many of the martensite crystals in the quenched microstructure are fractured or microcracked. This paper describes a process in which a limited amount of martensite is formed by quenching the steel to a temperature between the Ms temperature and conventional quench temperatures. This martensite is then tempered for a short time to toughen it before again cooling the steel to complete the formation of martensite from austenite. When the limited amount of martensite formed, and intermediately tempered, and the martensite formed on cooling from the intermediate tempering temperature are appropriately balanced by the processing, micro-cracking is essentially avoided. The process can be done in equipment and with procedures commonly used commercially.

Copyright © 1984 by ASME
Your Session has timed out. Please sign back in to continue.





Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In