Seizure Mechanism in Cold Extrusion and Forging

[+] Author and Article Information
Nozomu Kawai

Department of Mechanical Engineering, Nagoya University, Furō-chō, Chikusa-ku, Nagoya, Japan

Hiroyuki Saiki

Department of Production Mechanical Engineering, Kumamoto University, Kumamoto, Japan

Tamotsu Nakamura

Department of Mechanical Engineering, Shizuoka University, Hamamatsu, Japan

J. Eng. Mater. Technol 106(3), 257-263 (Jul 01, 1984) (7 pages) doi:10.1115/1.3225712 History: Received June 23, 1983; Online September 23, 2009

Abstract

To examine the seizure mechanism in cold extrusion and forging, a bifurcating extrusion type friction testing machine has been manufactured by the authors. This friction testing method was devised to simulate the frictional surface in the process accompanied with a remarkable surface expansion which influences markedly the seizure phenomena in extrusion and forging. Using a commercially pure aluminium as the workmetal, the frictional characteristics, and in particular the seizure mechanism, have been investigated under a lubricated condition with a mineral oil of higher viscosity and a dry frictional condition. Under the lubricated condition, the frictional surface was remarkably expanded more than 26 times; nevertheless no seizure was observed throughout the extruded travel. On the other hand, under the dry frictional condition, the seizure is initiated at the region where a virgin surface is exposed or the relative slip displacement exceeds a critical value. It was observed that even in the dry frictional condition, a smooth burnished metal surface could be obtained if the surface expansion ratio and the relative slip displacement are lower than a critical value.

Copyright © 1984 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In