Effect of Heat-Treatment Upon the Fatigue-Crack Growth Behavior of Alloy 718 Weldments—Part I: Macroscopic Behavior

[+] Author and Article Information
L. A. James, W. J. Mills

Westinghouse Hanford Co., Richland, WA 99352

J. Eng. Mater. Technol 107(1), 34-40 (Jan 01, 1985) (7 pages) doi:10.1115/1.3225768 History: Received August 29, 1983; Online September 23, 2009

Abstract

Gas-tungsten-arc weldments in Alloy 718 were studied in fatigue-crack growth tests conducted at five temperatures over the range 24–649°C. In general, crack growth rates increased with increasing temperature, and weldments given the “conventional” post-weld heat-treatment generally exhibited crack growth rates that were higher than for weldments given the “modified” (INEL) heat-treatment. Limited testing in the as-welded condition revealed crack growth rates significantly lower than observed for the heat-treated cases, and this was attributed to residual stresses. Three different heats of filler wire were utilized, and no heat-to-heat variations were noted.

Copyright © 1985 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In