Effect of Prior Deformation on the 76-K Fracture Toughness of AISI 304L and AWS 308L Stainless Steels

[+] Author and Article Information
P. T. Purtscher, D. T. Read

Fracture and Deformation Division, National Bureau of Standards, Boulder, Colo. 80303

J. Eng. Mater. Technol 109(2), 151-156 (Apr 01, 1987) (6 pages) doi:10.1115/1.3225955 History: Received July 29, 1986; Online September 15, 2009

Abstract

In this study, the effect of service-induced deformation on the toughness of AISI 304L and its weld metal, A WS 308L was determined. Low temperature compressive loading in the laboratory produced larger deformations. Crack initiation toughness, KIC (J), and tearing resistance, dJ/da, at 76 K were evaluated as a function of martensite content, a measure of the deformation in these steels. The results showed that the toughness properties of the 304L decrease gradually as the martensite content increases from the 5 to 8 percent level found in the service condition to the 45 percent level obtained by compressive loading. The decrease was less than that expected on the basis of the increased flow stress. The toughness properties of the 308L weld metal decreased more sharply with increased martensite content than those of the 304L. The sharp decrease is associated with a degradation of the properties of the delta ferrite rather than that of the austenite.

Copyright © 1987 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In