The Influence of Test Temperature on the Ratchetting Behavior of Type 304 Stainless Steel

[+] Author and Article Information
M. B. Ruggles, E. Krempl

Mechanics of Materials Laboratory, Rensselaer Polytechnic Institute, Troy, NY 12180-3590

J. Eng. Mater. Technol 111(4), 378-383 (Oct 01, 1989) (6 pages) doi:10.1115/1.3226483 History: Received March 08, 1988; Revised May 03, 1989; Online September 15, 2009

Abstract

The zero-to-tension ratchetting behavior was investigated under uniaxial loading at room temperature and at 550, 600, and 650°C. In History I the maximum stress level of ratchetting was equal to the stress reached in a tensile test at one percent strain. For History II the maximum stress level was established as the stress reached after a 2100 s relaxation at one percent strain. Significant ratchetting was observed for History I at room temperature but not at the elevated temperatures. The accumulated ratchet strain increases with decreasing stress rate. Independent of the stress rates used insignificant ratchet strain was observed at room temperature for History II. This observation is explained in the context of the viscoplasticity theory based on overstress by the exhaustion of the viscous contribution to the stress during relaxation. The viscous part of the stress is the driving force for the ratchetting in History I. Strain aging is presumably responsible for the lack of short-time inelastic deformation resulting in a nearly rate-independent behavior at the elevated temperatures.

Copyright © 1989 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In