Use of Subsized Specimen for Evaluating the Strength and Fracture Toughness of Irradiated 2 1/4 Cr-1 M0 Steel

[+] Author and Article Information
X. Mao, H. Takahashi, T. Kodaira

Department of Mechanical Engineering, University of Calgary, Calgary, Alberta, Canada T2N 1N4

J. Eng. Mater. Technol 114(2), 168-171 (Apr 01, 1992) (4 pages) doi:10.1115/1.2904157 History: Received August 01, 1990; Revised July 15, 1991; Online April 29, 2008

Abstract

The procedure of the determination of yield and ultimate strengths of irradiated 2 1/4 Cr-1 M0 steel using small punch specimen (10 mm by 10 mm by 0.5 mm) has been demonstrated. The result was compared with the result obtained from conventional tensile test. Fracture toughness of irradiated 2 1/4 Cr-1 M0 steel was measured by use of subsized CT specimen and D. C. electrical potential method. Owing to irradiation hardening of 2 1/4 Cr-1 M0 steel, yield and ultimate strength increase substantially and fracture toughness decreases 37 percent when the steel is irradiated to a fluence of 3.2 x 1023 n/m2 . The small punch and subsized CT specimen can be used for irradiation test so that considerable irradiation space will be saved.

Copyright © 1992 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In