Corrosion-Fatigue (Circumferential) Cracking in Cr-Mo Low Alloy Boiler Tube Steels: Part 1—Initiation and Propagation

[+] Author and Article Information
B. J. Smith, A. R. Marder

Energy Research Center, Lehigh University, Bethlehem, PA 18015

J. Eng. Mater. Technol 114(3), 265-269 (Jul 01, 1992) (5 pages) doi:10.1115/1.2904171 History: Received April 19, 1991; Revised November 29, 1991; Online April 29, 2008

Abstract

The metallurgical mechanism responsible for the initiation and propagation of circumferentially oriented, fireside cracks on waterwall boiler tubes was investigated. The materials studied were Cr-Mo low alloy steels in the as-received and post-service (exhibited cracking) condition. It was determined that cracks were initiated by a corrosion/fatigue interactive mechanism at the fireside tube surface. The corrosion mechanism is sulfidation while the material fatigue degradation occurs due to thermal stress cycles. Crack propagation occurs by an environmentally assisted thermal fatigue crack propagation mechanism.

Copyright © 1992 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us: