Influence of Environment and Creep on Fatigue Crack Growth in a High Temperature Aluminum Alloy 8009

[+] Author and Article Information
K. V. Jata

Wright Laboratory Materials Directorate, WL/MLSA, Wright-Patterson Air Force Base, OH 45433

D. Maxwell

University of Dayton Research Institute, Dayton, OH 45469

T. Nicholas

Wright Laboratory Materials Directorate, WL/MLLN, Wright-Patterson Air Force Base, OH 45433

J. Eng. Mater. Technol 116(1), 45-53 (Jan 01, 1994) (9 pages) doi:10.1115/1.2904254 History: Received December 23, 1992; Revised May 19, 1993; Online April 29, 2008

Abstract

Frequency effects on fatigue crack growth rates are examined in aluminum alloy 8009 in sheet and extruded product forms. The investigations show that frequency effects on the fatigue crack growth rates are pronounced in the sheet but minimal in the extrusion. The influence of creep cracking on fatigue crack growth rate is studied through tests with a 60 s hold-time at maximum load at several stress intensity ranges. A 60 s hold-time at maximum load at 315°C tends to retard fatigue crack growth in both the sheet and the extrusion. The mechanism by which this retardation occurs is attributed to stress relaxation at the crack tip. At 204°C a 60 s hold at Pmax accelerates crack growth rate in the sheet but not in the extrusion. Vacuum and laboratory air tests show that fatigue crack growth rates in vacuum are lower than in air by about a factor of four. A 60 s hold-time at minimum load has only a minor effect on the fatigue crack growth rates at 315°C and no effect at 204°C, confirming the absence of any strong environmental contribution to crack growth rate. Fracture modes in fatigue, creep crack growth and hold-time at Pmax are significantly different. The fractographic results are discussed in relation to the mechanical property data.

Copyright © 1994 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In