Thermomechanical Fatigue Behavior of a Quasi-lsotropic SCS-6/Ti-15-3 Metal Matrix Composite

[+] Author and Article Information
K. A. Hart, S. Mall

Department of Aeronautics and Astronautics, Air Force Institute of Technology, Wright Patterson Air Force Base, OH 45433

J. Eng. Mater. Technol 117(1), 109-117 (Jan 01, 1995) (9 pages) doi:10.1115/1.2804361 History: Received April 14, 1993; Revised May 06, 1994; Online November 27, 2007

Abstract

The response of a quasi-isotropic laminate of metal matrix composite, SCS-6/Ti-15-3 in a thermomechanical fatigue (TMF) environment was investigated. To achieve this, three sets of fatigue tests were conducted: 1) in-phase TMF (IP-TMF), 2) out-of-phase TMF (OP-TMF), and 3) isothermal fatigue (IF). The fatigue response was dependent on the test condition and the maximum stress level during cycling. The IF, IP-TMF, and OP-TMF conditions yielded shortest fatigue life at higher, intermediate and lower stress levels, respectively. Examination of the failure mode through the variation of strain or modulus during cycling, and post-mortem microscopic evaluation revealed that it was dependent on the fatigue condition and applied stress level. Higher stresses, mostly with IP-TMF and IF conditions, produced a primarily fiber dominated failure. Lower stresses, mostly with the OP-TMF condition, produced a matrix dominated failure. Also, an empirical model based on the observed damage mechanisms was developed to represent the fatigue lives for the three conditions examined here.

Copyright © 1995 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In