Carbide Coarsening During Creep in 12 Percent CrMoV Steel

[+] Author and Article Information
Rui Wu, Rolf Sandström

Division of Materials Technology, Department of Materials Science and Engineering, Royal Institute of Technology, S-100 44 Stockholm, Sweden

J. Eng. Mater. Technol 118(4), 485-492 (Oct 01, 1996) (8 pages) doi:10.1115/1.2805946 History: Received August 05, 1995; Revised June 02, 1996; Online November 27, 2007


Carbide coarsening has been investigated in a 12 percent CrMoV steel. Studies in the gauge length (creep exposed) and in the head (stress free ageing) for both interrupted and ruptured creep specimens tested at an initial stress of 80 MPa at various temperatures and at 600°C at different initial stresses have been performed. The measured quantities include hardness, carbide sizes in the tempered martensite, at the former austenite grain boundaries and at the δ-ferrite boundaries as well as mean free distance between carbides, total number of carbides, and carbide size distribution. The contributions to the increase of strain rate in the tertiary creep are discussed in terms of plastic deformation, cavitation accumulation, and microstructural degradation. By using a strain and strain rate relation, expressions to quantitatively account for each contribution to increase of strain rate are given. The increase of strain rate, thereby rupture, is mainly caused by the microstructural degradation due to carbide coarsening and by the cavitation accumulation.

Copyright © 1996 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.





Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In