Effect of Cure State on Stress Relaxation in 3501-6 Epoxy Resin

[+] Author and Article Information
S. R. White

Department of Aeronautical and Astronautical Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801

A. B. Hartman

Department of Mechanical and Industrial Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801

J. Eng. Mater. Technol 119(3), 262-265 (Jul 01, 1997) (4 pages) doi:10.1115/1.2812254 History: Received January 07, 1997; Revised April 03, 1997; Online November 27, 2007


Little experimental work has been done to characterize how the viscoelastic properties of composite material matrix resins develop during cure. In this paper, the results of a series of creep tests carried out on 3501–6 epoxy resin, a common epoxy matrix material for graphite/epoxy composites, at several different cure states is reported. Beam specimens were isothermally cured at increasing cure temperatures to obtain a range of degrees of cure from 0.66 to 0.99. These specimens were then tested in three-point bending to obtain creep compliance over a wide temperature range. The master curves and shift functions for each degree of cure case were obtained by time-temperature superposition. A numerical technique and direct inversion were used to calculate the stress relaxation modulus master curves from the creep compliance master curves. Direct inversion was shown to be adequate for fully cured specimens, however it underpredicts the relaxation modulus and the transition for partially cured specimens. Correlations with experimental stress relaxation data from Kim and White (1996) showed that reasonably accurate results can be obtained by creep testing followed by numerical conversion using the Hopkins-Hamming method.

Copyright © 1997 by The American Society of Mechanical Engineers
Your Session has timed out. Please sign back in to continue.





Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In