Determination of Interface Fracture Toughness in Thermal Barrier Coating System by Blister Tests

[+] Author and Article Information
Y. C. Zhou

Fracture Research Institute, Tohoku University, Sendai 980-8579, JapanInstitute of Fundamental Mechanics and Material Engineering, Xiangtan University, Xiangtan, Hunan, 411105, P. R. China

T. Hashida, C. Y. Jian

Fracture Research Institute, Tohoku University, Sendai 980-8579, Japan

J. Eng. Mater. Technol 125(2), 176-182 (Apr 04, 2003) (7 pages) doi:10.1115/1.1555658 History: Received February 07, 2001; Revised May 29, 2002; Online April 04, 2003
Copyright © 2003 by ASME
Your Session has timed out. Please sign back in to continue.


Amagasa,  S., and Shimomura,  K., , 1994, “Study on the Turbine Vane and Blade for a 1500°C Class Industrial Gas Turbine,” ASME J. Eng. Gas Turbines Power, 116, pp. 597–604.
Yuri,  I., Hisamatsu,  T., Watanabe,  K., and Etori,  Y., 1997, “Structural Design and High Pressure Test of a Ceramic Combustor for 1500°C Class Industrial Gas Turbine,” ASME J. Eng. Gas Turbines Power, 119, pp. 506–511.
Zhu,  D. M., and Miller,  R. A., 1999, “Determination of Creep Behavior of Thermal Barrier Coatings Under Laser Imposed High Thermal and Stress Gradient Conditions,” J. Mater. Res., 14, pp. 146–161.
Jian,  C. Y., and Hashida,  T., 1995, “Thermal Shock and Fatigue Resistance Evaluation of Functionally Graded Coating for Gas Turbine Blades by Laser Heating Method,” Composites Eng., 5, pp. 879–889.
Zhou,  Y. C. and Hashida,  T., 2002, “Thermal Failure Induced by Delamination in Thermal Barrier Ceramic Coating,” Int. J. Fatigue, 24, pp. 407–417.
Ogawa,  K., Minkov,  D., Shoji,  T., Sato,  M., and Hashimoto,  H., 1999, “NDE of Degradation of Thermal Barrier Coating by Means of Impedance Spectroscopy,” NDT & E Int., 32, pp. 177–185.
Cheng,  J., Jordan,  E. H., Barber,  B., and Gell,  M., 1998, “Thermal/Residual Stress in an Electron Beam Physical Vapor Deposited Thermal Barrier Coating System,” Acta Mater., 46, pp. 5839–5850.
Zhou,  Y. C., and Hashida,  T., 2001, “Coupled Effects of Temperature Gradient and Oxidation on the Thermal Stress in Thermal Barrier Coating System,” Int. J. Solids Struct., 38, pp. 4235–4264.
Zhou, Y. C., and Hashida, T., 2002, “Delamination Cracking in Thermal Barrier Coating System,” ASME J. Eng. Gas Turbines Power, in press.
He,  M. Y., Evans,  A. G., and Hutchinson,  J. W., 1998, “Effects of Morphology on the Decohesion of Compressed Thin Films,” Mater. Sci. Eng., A, 245, pp. 168–181.
Bernstein,  H. L., and Allen,  J. M., 1992, “Analysis of Cracked Gas Turbine Blades,” ASME J. Eng. Gas Turbines Power, 114, pp. 293–301.
Cruse,  T. A., Stewart,  S. E., and Ortiz,  M., 1998, “Thermal Barrier Coating Life Prediction Model Development,” ASME J. Eng. Gas Turbines Power, 110, pp. 610–616.
Bartlett,  A. H., and Maschio,  R. D., 1995, “Failure Mechanisms of a zirconia-8wt% yttria Thermal Barrier Coating,” J. Am. Ceram. Soc., 78, pp. 1018–1024.
Hutchinson,  J. W., and Suo,  Z., 1992, “Mixed Mode Cracking in Layered Materials,” Adv. Appl. Mech., 29, pp. 63–191.
Evans,  G., and Hutchinson,  J. W., 1995, “The Thermomechanical Integrity of Thin Films and Multilayers,” Acta Metall. Mater., 43, pp. 2507–2530.
Dannenberg,  H., 1961, “Measurement of Adhesion by a Blister Method,” J. Appl. Polym. Sci., 5, pp. 125–134.
Gent,  A. N., and Lewandowski,  L. H., 1987, “Blow-Off Pressure for Adhering Layers,” J. Appl. Polym. Sci., 33, pp. 1567–1577.
Shirani,  A., and Liechti,  K. M., 1998, “A Calibrated Fracture Process Zone Model for Thin Film Blistering,” Int. J. Fract., 93, pp. 281–314.
Jensen,  H. M., and Thouless,  M. D., 1993, “Effects of Residual Stresses in the Blister Test,” Int. J. Solids Struct., 30, pp. 779–795.
Clyne,  T. W., and Gill,  S. C., 1996, “Residual Stresses in Thermal Spray Coatings and Their Effect on Interfacial Adhesion: A Review of Resent Work,” J. Thermal Spray Tech., 5 , pp. 401–418.
Clyne,  T. W., 1996, “Residual Stresses in Surface Coatings and Their Effects on Interfacial Debonding,” Key Eng. Mater., 116, pp. 307–330.
Ohnabe,  H., and Mizuguchi,  F., 1993, “Large Deflections of Heated Non-Homogenous Circular Plates With Radially Varying Rigidity,” Int. J. Non-Linear Mech., 28, pp. 365–372.
Zhou,  Y. C., Duan,  Z. P., and Yang,  Q. B., 1998, “Shear Deformation Analysis on Laser-Induced Reverse Bulging and Plugging,” Int. J. Non-Linear Mech., 33, pp. 433–446.
Berger,  H. M., and Washington,  D. C., 1955, “A New Approach to the Analysis of Large Deflections of Plates,” J. Appl. Mech., 22, pp. 465–472.
Suo,  Z. G., and Hutchinson,  J. W., 1990, “Interface Crack Between Two Elastic Layers,” Int. J. Fract., 43, pp. 1–18.
Dundurs,  J., 1969, “Edge-Bonded Dissimilar Orthogonal Elastic Wedges Under Normal and Shear Loading,” ASME J. Appl. Mech., 36, pp. 650–652.
Hillery, R. V., and Pllsner, B. H., 1988, NASA Technical Report, NASA CR-180807.
Chung,  B. T. F., Kermani,  M. M., Braun,  M. J., , 1985, “Heat Transfer in Thermal Barrier Coated Rods With Circumferential and Radial Temperature Gradients,” ASME J. Eng. Gas Turbines Power, 107, pp. 135–141.
Evans,  A. G., and Dalgleish,  B. J., 1992, “The Fracture Resistance of Metal-Ceramic Interfaces,” Acta Mater., 40, pp. S295–S306.
Wang,  J. S., 1998, “A Micromechanical Model for Interface Crack Extension in Metal/Ceramic Bimaterial Systems,” Acta Mater., 46, pp. 4973–4984.
International Society for Rock Mechanics, 1988, “Suggested Methods for Determining the Fracture Toughness of Rock,” Int. J. Rock Mech. Min. Sci., 25 , pp. 71–96.
Matejicek, J., Sampath, S., and Dubsky, J., “X-Ray Residual Stress Measurement in Metallic and Ceramic Plasma Sprayed Coatings,” J. Thermal Spray Tech., 74 , pp. 489–496.
Evans,  A. G., and Hutchinson,  J. W., 1989, “Effects of Non-Planarity on the Mixed Mode Fracture Resistance of Biomaterial Interfaces,” Acta Metall., 37, pp. 909–916.


Grahic Jump Location
Comparison of interface crack length determined by the compliance method and SEM observation
Grahic Jump Location
Interface crack propagation curves, where NO.1∼NO.9 indicate experimental order for type A coating, NO.10∼12 indicates experimental order for type B coating
Grahic Jump Location
Variation of mode mixty parameter versus interface crack extension, where NO.1∼NO.9 indicates experimental order for type A coating, NO.10∼NO.12 indicate experimental order for type B coating
Grahic Jump Location
Configuration for the test as an experimental procedure for interface toughness measurement
Grahic Jump Location
Specimen configuration and dimensions used for the blister test
Grahic Jump Location
Schematic of experimental set-up for the blister test
Grahic Jump Location
Microstructure of PSZ coating layer with different porosity: (a) Type A, dense coating; and (b) Type B, porosity coating
Grahic Jump Location
SEM observation of interface crack induced by the blister test: (a) focusing on the interface crack tip, and (b) the full view of the interface crack
Grahic Jump Location
Oil pressure q versus the maximum deflection w(0) for the debonded coating
Grahic Jump Location
Principles of compliance method with the construction of linearization for unloading-reloading cycle



Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In